Taguchi method was used to predict and optimize the effects of hygrothermal aging on the tensile behavior of asymmetric helicoidally stacked Carbon Fiber Reinforced Plastic (CFRP) composites. This research is in furtherance to the previous work, which dealt purely with experiments. MR70 12P carbon fiber epoxy prepreg sheets were manufactured into laminated composites comprising constant inter-ply pitch angles ranging from 0o to 30o. The composites were tested in tension as either dry unaged specimens or following hygrothermal aging in seawater at the constant temperatures of 40 oC and 60 oC for 2000 hrs. Optimizations were conducted based on Taguchi L18 orthogonal array considering two design parameters viz. inter-ply stacking angles and hygrothermal aging temperature. The result depicted that the combination of aging temperature (C) and stacking angles are major factors in determining the tensile behavior of composite materials (p = 0.011). The model explains 86.6% of tensile strength variability, with a predicted R-squared value of 93.04%. The model’s robustness is supported by the adjusted R-squared value of 77.6%. Analysis of variance shows that inter-ply stacking angles are the main significant factor affecting the tensile behaviors at a 95% confidence level. A confirmation test was carried out to validate the optimized results and it was found that there were improvements in S/N ratios from initial to optimal setting.
Keywords:
Published on: Oct 17, 2023 Pages: 68-72
Full Text PDF
Full Text HTML
DOI: 10.17352/2455-488X.000071
CrossMark
Publons
Harvard Library HOLLIS
Search IT
Semantic Scholar
Get Citation
Base Search
Scilit
OAI-PMH
ResearchGate
Academic Microsoft
GrowKudos
Universite de Paris
UW Libraries
SJSU King Library
SJSU King Library
NUS Library
McGill
DET KGL BIBLiOTEK
JCU Discovery
Universidad De Lima
WorldCat
VU on WorldCat
PTZ: We're glad you're here. Please click "create a new query" if you are a new visitor to our website and need further information from us.
If you are already a member of our network and need to keep track of any developments regarding a question you have already submitted, click "take me to my Query."